TY - JOUR ID - 82341 TI - Control of Formation of Intermetallic Compound in Dissimilar Joints Aluminum-steel JO - International Journal of Engineering JA - IJE LA - en SN - 1025-2495 AU - Hincapié, O. D. AU - Salazar, J. A. AU - Restrepo, J. J. AU - Torres, E. A. AU - Graciano-Uribe, J. AD - Department of Mechanical Engineering, Research Group – GEA, Universidad de Antioquia, Medellín, Colombia AD - Department of Mechatronics Engineering, Research Group - MATyER, Instituto Tecnológico Metropolitano, Medellín, Colombia Y1 - 2019 PY - 2019 VL - 32 IS - 1 SP - 127 EP - 136 KW - Dissimilar Joints KW - heat input KW - FexAly Compounds KW - Friction welding DO - N2 - The elimination of the FexAly type phases was considered the solution to low ductility presented in aluminum-steel welded joints. Recently, the researches do not seek the suppression but the control of the thickness of these compounds. In this work, Al-Fe joints were manufactured by solid state and fusion welding, looking for controlling the formation of intermetallic compounds. Temperature measurements were carried out during the welding. The joints interface was characterized using optical and scanning electronic microscopy, aided by chemical composition measures with X-EDS. The microstructural characterization at the interface of aluminum-steel joints, in solid state welded joints, demonstrated the absence of intermetallic compounds, which is attributed to the low temperature reached during the process - less than 300 ° C. In the case of fusion joints, it has observed the permanent formation of intermetallic compounds whose thickness varies significantly with the heat input. UR - https://www.ije.ir/article_82341.html L1 - https://www.ije.ir/article_82341_170f483386a96d9122fe6de40d23a83c.pdf ER -