TY - JOUR ID - 71845 TI - Preparation of Cobalt Oxide/Zinc Oxide Nanocomposite JO - International Journal of Engineering JA - IJE LA - en SN - 1025-2495 AU - Alibeigi, S. AU - Vaezi, M.R. AU - Nikzad, L. AU - Esmaielzadeh Kandjani, A. AD - materials department, KNTU AD - Nanotechnology and Advanced Materials Department, Material and Energy Research Center(MERC) AD - Research Center of Advanced Materials, Merc AD - Applied Science, RMIT - RMIT University Y1 - 2010 PY - 2010 VL - 23 IS - 2 SP - 133 EP - 138 DO - N2 - Cobalt Oxide/ Zinc Oxide nanocomposite was synthesized by dropwise addition ofCo(NO)3.6H2O and Zn(NO3)2.4H2O solutions to KOH solution at different temperatures followed bycalcination at 300ºC for 4 h. The morphology and structure of nanoparticles and the influence oftemperature on particle size were studied using scanning electron microscopy (SEM) and X-RayDiffraction (XRD). Minimum particle size was obtained before calcination at 70ºC. In addition, thespherical, semispherical and flake-shaped nanoparticles were observed at ambient temperature. Onthe other hand, Co(OH)2 was transformed to Co3O4, ZnO flakes were eliminated, and particle sizechanged during calcination. Synthesized samples at 50ºC and 70ºC showed an increase size aftercalcinations; however, elimination of flakes during calcination caused particle size reduction forsynthesized sample at ambient temperature. UR - https://www.ije.ir/article_71845.html L1 - https://www.ije.ir/article_71845_a91c606002eca76d53440ed34f8103d0.pdf ER -